Dielectric composition and multilayer ceramic capacitor embedded low temperature co-fired ceramic substrate using the same

ABSTRACT

Provided are a dielectric composition and a multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate using the same. The dielectric composition includes a main component, BaTiO 3  of about 80 wt % or more, and an accessory component, CuBi 2 O 4  and ZnO—B 2 O 3 —SiO 2 -based glass of about 20 wt % or less.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the priority of Korean Patent Application No. 2007-0122993 filed on Nov. 29, 2007, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a dielectric composition and a multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate using the same, and more particularly, to a dielectric composition and a multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate using the same, which is sinterable at a low temperature while showing a high dielectric constant.

2. Description of the Related Art

Recently, a technology of reducing a total volume of a product and increasing the degree of integration of a substrate not by mounting a device such as a surface mount device on the surface of the substrate but by embedding the device into a substrate having a circuit pattern is receiving attention according to the miniaturization and high frequency tendency of various electrical products.

When a chip-typed device on the substrate is replaced with a layer-typed device (e.g., a capacitor), an increase of the volume caused by the chip may be suppressed. Also, the layer-typed capacitor has more excellent high-frequency property (e.g., smaller parasitic inductance) than the chip-typed capacitor. Accordingly, various attempts have been made to embed the chip into the substrate.

A Printed Circuit Board (PCB) is generally divided into two types according to materials forming a dielectric layer. One PCB applied with a polymeric organic material as a dielectric layer is more widely used. A plating method is used to form a circuit pattern on the PCB. On the other hand, a screen printing is mainly used to form the circuit pattern on the other PCB, the dielectric layer of which is formed of a ceramic material. In this case, the PCB is manufactured by sintering the dielectric layer and an electrode simultaneously. The sintering process is generally performed at a temperature of about 800° C. or more.

Two types of substrates have very different properties in the aspects of a material and a manufacturing process. However, their structures are very similar to each other in that the circuit pattern is formed in a laminated body of multilayer. Accordingly, their applicable ranges overlap each other in many cases. There are few technologies to which both types of substrates may be together applied because the material and the manufacturing process of each type is entirely different from each other as described above.

In a case where the capacitor is embedded into the ceramic substrate, a dielectric layer for a capacitor and an internal electrode are formed and simultaneously sintered between ceramic green sheets including a ceramic and a glass. In case of the capacitor, the dielectric constant property is important. BaTiO₃ may be used as a main component of composition used in the dielectric layer instead of Pb because of a high dielectric constant and environmental reason. However, BaTiO₃ may be sintered at a temperature of about 1400° C. or more unless a sintering additive is used. Moreover, although the sintering additive is used, BaTiO₃ is difficult to be sintered at a temperature of about 1000° C. or less.

In a ceramic substrate embedded with the capacitor, the dielectric constant and the sinterable temperature are important. In case of the ceramic substrate, an electrode is formed by printing a metal such as Ag or Cu, which is sintered to form a circuit pattern on the substrate. Accordingly, the firing temperature of the ceramic substrate must be lower than at least the melting points of Ag and Cu. However, when the capacitor is embedded, the firing temperature of the capacitor must be lower than at least the melting points of Ag and Cu because the embedded capacitor must be together sintered. In this case, as described above, the dielectric layer may not be completely sintered. Moreover, the dielectric constant may be reduced.

Accordingly, the development of a technology capable of manufacturing a low temperature co-fired ceramic substrate embedded with a multi-layer ceramic capacitor showing a high dielectric constant after even a low temperature firing is required.

SUMMARY OF THE INVENTION

An aspect of the present invention provides to a dielectric composition and a multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate using the same, which is sinterable at a low temperature while showing a high dielectric constant.

According to an aspect of the present invention, there is provided a dielectric composition including: a main component, BaTiO₃ of about 80 wt % or more; and an accessory component, CuBi₂O₄ and ZnO—B₂O₃—SiO₂-based glass of about 20 wt % or less.

The content of CuBi₂O₄ may be about 4 wt % to about 10 wt % relative to a total weight of BaTiO₃. Also, the content of ZnO—B₂O₃—SiO₂-based glass may be about 1 wt % to about 5 wt % relative to the total weight of BaTiO₃.

Especially, the content of CuBi₂O₄ may be about 6 wt % relative to the total weight of BaTiO₃, and the content of ZnO—B₂O₃—SiO₂-based glass may be about 4 wt % relative to the total weight of BaTiO₃.

The content of ZnO may be about 50 wt % to about 90 wt % relative to a total weight of the glass.

A mean particle diameter of BaTiO₃ may be about 500 nm or less.

A sintering temperature may be about 600° C. to about 950° C.

According to another aspect of the present invention, there is provided a multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate including: a ceramic laminated body laminated with a plurality of ceramic green sheets printed with a ceramic sheet internal electrode; a plurality of dielectric layers formed in the ceramic laminated body, the dielectric layers embedded with a multi-layer ceramic capacitor including a dielectric composition including a main component, BaTiO₃ of about 80 wt % and an accessory component, CuBi₂O₄ and ZnO—B₂O₃—SiO₂ of-based glass of about 20 wt %; and a plurality of capacitor internal electrodes formed between the dielectric layers, and electrically connected to the ceramic sheet internal electrode.

The content of CuBi₂O₄ may be about 4 wt % to about 10 wt % relative to a total weight of BaTiO₃.

The ceramic sheet internal electrode may include one of Ag and Cu. Also, a firing temperature may be about 600° C. to about 950° C.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other aspects, features and other advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:

FIG. 1 is a sectional view illustrating a multi-layer ceramic capacitor according to an embodiment of the present invention; and

FIG. 2 is a scanning electron micrograph illustrating a sintered dielectric composition according to an embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

Hereinafter, exemplary embodiments of the present invention will now be described in detail with reference to the accompanying drawings. The exemplary embodiments of the present invention may be modified into various forms. Also, the scope of the present invention should not be construed as limited to the below embodiments. It will be noted that the exemplary embodiments of the present invention are provided for those skilled in the art to more completely understand the present invention. Therefore, the shape and size of elements shown in the drawings may be exaggerated for clarity.

A dielectric composition according to an embodiment of the present invention includes a main component, BaTiO₃ of about 80 wt % or more, and an accessory component, CuBi₂O₄ and ZnO—B₂O₃—SiO₂-based glass of about 20 wt % or less.

For the dielectric constant of the dielectric composition according to an embodiment of the present invention, BaTiO₃ may be used as a ceramic filler. As described above, in order to show a desired level of the dielectric constant, Pb has been generally used as a filler. However, due to an environmental reason of Pb, BaTiO₃ instead of Pb is used as a ceramic filler, which is the main component of the composition used in the dielectric layer.

A particle diameter of the filler affects the dielectric constant and the low temperature sintering. If the particle diameter is smaller, the sintering is easier. If the particle diameter is greater, the sintering is more difficult. Accordingly, a mean particle diameter of the main component BaTiO₃ is preferably about 500 nm or less.

BaTiO₃ may be sintered at a temperature of about 1400° C. or more unless a sintering additive inducing a low temperature firing is used. Moreover, although the sintering additive is used, BaTiO₃ is difficult to be sintered at a temperature of about 1000° C. or less. Accordingly, the CuBi₂O₄ and ZnO—B₂O₃—SiO₂-based glass are together used in order to form the dielectric composition.

In the dielectric composition, the content increase of the filler is one way of increasing the dielectric constant. However, when the content of the filler is high, there is a limitation in the low temperature sintering. Accordingly, besides BaTiO₃, a component capable of reducing the sintering temperature must be included.

According to an embodiment of the present invention, besides the main component BaTiO₃, CuBi₂O₄ and ZnO—B₂O₃—SiO₂ are used as an accessory component. CuBi₂O₄ serves to lower the sintering temperature to a temperature of about 800° C. to about 900° C. CuBi₂O₄ is a crystalline ceramic compound formed by mixing CuO and Bi₂O₃.

The content of CuBi₂O₄ is preferably about 4 wt % to about 10 wt % relative to the total weight of BaTiO₃. If the content of CuBi₂O₄ is too low, the effect on the sintering temperature of the entire dielectric composition is insignificant. If the content of CuBi₂O₄ is too high, the dielectric constant may be lowered.

Besides CuBi₂O₄, the ZnO—B₂O₃—SiO₂-based glass may be added as an accessory component. The ZnO—B₂O₃—SiO₂-based glass serves to lower the sintering temperature of the dielectric composition as well as the dielectric loss. The content of the ZnO—B₂O₃—SiO₂-based glass is preferably about 50 wt % to about 90 wt % relative to the total weight of the glass.

If the content of the ZnO—B₂O₃—SiO₂-based glass is too low similarly to CuBi₂O₄, the effects on reduction of the sintering temperature and the dielectric loss of the entire composition are too insignificant. If the content of ZnO—B₂O₃—SiO₂ is too high, the dielectric constant maybe lowered. In consideration of this point, the content of ZnO—B₂O₃—SiO₂-based glass is preferably about 1 wt % to 5 wt % relative to the total weight of BaTiO₃.

In order to maximally lower the dielectric loss while lowering the sintering temperature to about 950° C. or less, the contents of CuBi₂O₄ and the ZnO—B₂O₃—SiO₂-based glass are preferably about 6 wt % and about 4 wt %, respective.

Although BaTiO₃ is used as a main component of the dielectric composition including BaTiO₃ as a ceramic filler and CuBi₂O₄ and the ZnO—B₂O₃—SiO₂-based glass as an accessory component, the sintering temperature may be about 600° C. to about 950° C. Even in this temperature range, the dielectric composition according to the present invention is sinterable, and shows a relatively high dielectric constant.

In order to manufacture the dielectric composition according to the present invention, first, the main component BaTiO₃, and the accessory components CuBi₂O₄ and the ZnO—B₂O₃—SiO₂-based glass may be weighed to be a predetermined content, respectively, and manufactured into a slurry form using appropriate additive and solvent. The dielectric slurry is formed into dielectric sheets, which are laminated on each other. This dielectric composition is embedded into a low temperature co-fired ceramic substrate as a multi-layer ceramic capacitor as described below.

According to another embodiment of the present invention, a multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate is provided. The substrate includes a ceramic laminated body laminated with a plurality of ceramic green sheets printed with a ceramic sheet internal electrode, and a plurality of dielectric layers formed in the ceramic laminated body. The dielectric layer is embedded with a multi-layer ceramic capacitor including a dielectric composition having a main component BaTiO₃ of about 80 wt % and accessory components, CuBi₂O₄ and ZnO—B₂O₃—SiO₂-based glass of about 20 wt %. The plurality of capacitor internal electrodes are formed between the dielectric layers, and electrically connected to the ceramic sheet internal electrode.

FIG. 1 is a sectional view illustrating a multi-layer ceramic capacitor (MLCC) embedded low temperature co-fired ceramic (LTCC) substrate 100 according to an embodiment of the present invention. Hereinafter, the MLCC embedded LTCC will be described with reference to FIG. 1. However, description of the dielectric composition will be omitted because the dielectric composition has been already described above.

A MLCC embedded LTCC substrate 100 according to the present invention includes a ceramic laminated body 110, ceramic internal electrodes 121 and 122, and a multi-layer ceramic capacitor 130. The ceramic laminated body 110 is laminated with a plurality of ceramic green sheets 111, 112, 113 and 114. The ceramic sheet internal electrodes 121 and 122 are printed in the plurality of ceramic green sheets 111, 112, 113 and 114. The multi-layer ceramic capacitor 130 is embedded into the ceramic laminated body 110.

The ceramic sheet internal electrodes 121 and 122 are electrodes for an electrical connection between the ceramic green sheets 111, 112, 113 and 114, an electrical connection between the ceramic green sheets 111, 112, 113 and 114 and the multi-layer ceramic capacitor 130, and an electrical connection between the MLCC embedded LTCC substrate 100 and an external power source. The MLCC embedded LTCC substrate 100 may be connected to the external power source by forming an external electrode at the ceramic sheet internal electrode 121 exposed to the outside.

Referring to FIG. 1, the ceramic sheet internal electrodes 121 and 122 include a via-typed electrode 121 and a pad-typed electrode 122. The MLCC embedded LTCC substrate 100 includes capacitor external connection electrodes 151 and 152 for connecting capacitor internal electrodes 141, 142, 143, 144 and 145 of the multi-layer ceramic capacitor 130 to the pad-typed ceramic sheet internal electrode 122.

The ceramic sheet internal electrodes 121 and 122, and the capacitor external connection electrodes 151 and 152 may include one of Ag and Cu. Ag or Cu is a metal representing a most excellent performance in the aspect of the electrical conductivity. Accordingly, Ag or Cu may be used as a desirable metallic electrode without any disadvantage while showing an excellent electrical conductivity at a low temperature sintering of about 600° C. to about 950° C.

The ceramic green sheets 111, 112, 113 and 114 include a ceramic filler and a glass component. The ceramic filler usable in the ceramic green sheets 111, 112, 113 and 114 may be a filler sinterable at a low temperature in consideration of the low temperature firing, even if not, may be densified due to a viscous flow caused by the sintering of the glass component. Alumina or Titania may be used as a ceramic filler. The glass may include B₂O₃, SiO₂, Al₂O₃, and CaO.

The ceramic green sheets 111, 112, 113 and 114 is formed into a sheet form by mixing the filler, the glass and a bonding agent for bonding the glass and the filler in the solvent. Besides, additives such as a dispersing agent for the improvement of physical properties may be added to the ceramic green sheets 111, 112, 113 and 114.

The multi-layer ceramic capacitor 130 includes a plurality of dielectric layers 131, 132, 133, 134, 135 and 136, and a plurality of capacitor internal electrodes 141, 142, 143, 144 and 145, which are formed between a plurality of dielectric layers 131, 132, 133, 134, 135 and 136, and electrically connected to the ceramic sheet internal electrodes 121 and 122.

The dielectric layers 131, 132, 133, 134, 135 and 136 may include a main component BaTiO₃ of about 80 wt %, and accessory components CuBi₂O₄ and ZnO—B₂O₃—SiO₂-based glass of about wt %. The MLCC embedded LTCC substrate 100 sinterable at a low temperature as well as representing the high dielectric constant may be obtained by suppressing the property of BaTiO₃ sintered at a high temperature. The firing temperature of the MLCC embedded LTCC substrates 100 according to the present invention may be about 600° C. to about 950° C. like a general low temperature co-fired ceramic substrate.

The capacitor internal electrodes 141, 142, 143, 144 and 145 may include a highly electrically conductive metal, e.g. one of Ag, Cu and Ni.

Embodiment

Hereinafter, the exemplary embodiment of the present invention will be more fully described, but not limited thereto. The firing temperature, the dielectric constant and the dielectric loss (dissipation factor: DF) of the dielectric composition according to the embodiments of the present invention were measured.

First, the firing temperature, the dielectric constant and the dielectric loss of the dielectric composition including only one of CuBi₂O₄ and ZnO—B₂O₃—SiO₂ were measured in comparative examples 1 to 5. The result of the measurement is shown in Table 1 below. The measurement was twice performed with respect to the dielectric composition in each comparative example.

TABLE 1 Sintering temperature Linear CuBi₂O₄ ZnO—B₂O₃—SiO₂ BaTiO₃ size (° C.) shrinkage Dielectric Df (Content) (Proportion) (nm) (hour) rate (%) constant (%) Comparative CuBi₂O₄ — 150 975 26.7 2617 7.50 example 1 6 wt % 150 925 28.4 1205 9.50 Comparative CuBi₂O₄ — 50 870 13.8 506 275.00 example 2 6 wt % 50 (4 hour) 13.8 226 6.80 Comparative CuBi₂O₄ — 50 910 19.1 1066 90.00 example 3 6 wt % 50 (4 hour) 19.1 471 5.90 Comparative CuBi₂O₄ — 150 890 13.8 1294 63.60 example 4 10 wt % 150 13.8 732 5.90 Comparative CuBi₂O₄ — 150 925 23.8 1914 16.70 example 5 10 wt % 150 23.8 1303 8.50 Comparative — ZnO—B₂O₃—SiO₂ (7:2:1) 150 890 10.9 314 0.77 example 6 5 wt % 150 10.9 291 1.00 Comparative — ZnO—B₂O₃—SiO₂ (7:2:1) 150 925 17.5 604 0.83 example 7 5 wt % 150 17.5 550 0.96 Comparative — ZnO—B₂O₃—SiO₂ (6:2:2) 150 870 17.3 356 65.70 example 8 6 wt % 150 (4 hour) 17.3 178 1.70 Comparative — ZnO—B₂O₃—SiO₂ (6:2:2) 150 890 18.3 413 52.60 example 9 6 wt % 150 (4 hour) 18.3 260 2.00 Comparative — ZnO—B₂O₃—SiO₂ (6:2:2) 150 910 20.2 395 29.00 example 10 6 wt % 150 (4 hour) 20.2 308 1.30

The firing temperature, the dielectric constant and the dielectric loss of the dielectric composition including both CuBi₂O₄ and ZnO—B₂O₃—SiO₂ were measured in examples 1 to 32. The result of the measurement is shown in Table 2 below. The measurement was twice performed with respect to the dielectric composition in each example.

TABLE 2 Sintering ZnO—B₂O₃—SiO₂ Temperature Linear CuBi₂O₄ (Proportion) BaTiO₃ size (° C.) shrinkage Dielectric Example (Content) (Content) (nm) (hour) rate (%) constant Df (%) Example 1 CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 900 16.6 1051 14.60 6 wt % 0.5 wt % 150 (4 hour) 16.6 906 4.60 Example 2 CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 900 24.2 1346 3.40 6 wt % 1 wt % 150 (4 hour) 24.2 1167 5.40 Example 3 CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 900 24.2 714 3.10 6 wt % 2 wt % 150 (4 hour) 24.2 631 3.50 Example 4 CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 890 21.1 1427 2.90 6 wt % 2 wt % 150 21.1 954 5.10 Example 5 CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 925 25.0 1523 2.80 6 wt % 2 wt % 150 25.0 1309 5.40 Example 6 CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 890 23.8 1112 8.00 6 wt % 4 wt % 150 23.8 951 2.90 Example 7 CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 925 25.0 609 1.80 6 wt % 4 wt % 150 25.0 558 2.85 Example 8 CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 890 19.2 1106 21.30 6 wt % 6 wt % 150 19.2 897 2.50 Example 9 CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 925 24.9 889 11.00 6 wt % 6 wt % 150 24.9 702 4.00 Example CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 890 22.1 854 15.50 10 6 wt % 8 wt % 150 22.1 690 2.50 Example CuBi₂O₄ ZnO—B₂O₃—SiO₂ (7:2:1) 150 900 24.2 514 3.00 11 6 wt % 8 wt % 150 24.2 466 2.60 Example (CuBi₂O₄ + Bi₂O₃ 1:1) ZnO—B₂O₃—SiO₂ (7:2:1) 150 890 15.1 576 9.10 12 6 wt % 4 wt % 150 15.1 517 1.90 Example (CuBi₂O₄ + Bi₂O₃ 1:1) ZnO—B₂O₃—SiO₂ (7:2:1) 150 900 19.2 894 7.10 13 6 wt % 4 wt % 150 19.2 793 2.60 Example (CuBi₂O₄ + Bi₂O₃ 1:1) ZnO—B₂O₃—SiO₂ (7:2:1) 150 890 18.1 734 15.20 14 6 wt % 6 wt % 150 18.1 629 1.90 Example (CuBi₂O₄ + Bi₂O₃ 1:1) ZnO—B₂O₃—SiO₂ (7:2:1) 150 900 21.2 813 10.40 15 6 wt % 6 wt % 150 21.2 707 2.50 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 50 870 22.9 954 35.00 16 2 wt % 50 (4 hour) 22.9 564 5.10 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 50 890 23.3 844 22.00 17 2 wt % 50 (4 hour) 23.3 583 4.70 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 50 910 24.7 718 7.80 18 2 wt % 50 (4 hour) 24.7 579 4.50 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 50 870 21.4 545 14.00 19 4 wt % 50 (4 hour) 21.4 425 4.00 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 50 890 22.8 513 7.60 20 4 wt % 50 (4 hour) 22.8 426 4.00 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 50 910 24.1 532 8.00 21 4 wt % 50 (4 hour) 24.1 439 4.00 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 50 890 17.7 853 137.00 22 6 wt % 50 (4 hour) 17.7 363 6.30 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (6:2:2) 150 870 20.8 1091 80.00 23 2 wt % 150 (4 hour) 20.8 487 5.70 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (6:2:2) 150 890 23.0 875 57.60 24 2 wt % 150 (4 hour) 23.0 472 3.90 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (6:2:2) 150 910 24.7 708 26.00 25 2 wt % 150 (4 hour) 24.7 509 3.20 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (6:2:2) 150 870 22.4 630 29.50 26 4 wt % 150 (4 hour) 22.4 451 4.50 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (6:2:2) 150 890 23.2 638 19.70 27 4 wt % 150 (4 hour) 23.2 494 4.10 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (6:2:2) 150 910 23.8 649 13.80 28 4 wt % 150 (4 hour) 23.8 535 3.80 Example CuBi₂O₄ 4 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 100 890 22.3 792 3.80 29 2 wt % 100 22.3 682 4.60 Example CuBi₂O₄ 4 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 100 910 23.5 766 2.30 30 2 wt % 100 23.5 672 4.20 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 100 890 22.6 748 4.80 31 2 wt % 100 22.6 623 4.30 Example CuBi₂O₄ 6 wt % ZnO—B₂O₃—SiO₂ (7:2:1) 100 910 23.5 684 3.70 32 2 wt % 100 23.5 580 4.20

Referring to Table 1, in the comparative examples 1 to 5, only was added without to manufacture the dielectric composition. On the other hand, only ZnO—B₂O₃—SiO₂ was added without CuBi₂O₄ in the comparative examples 6 to 10. In this case, the sintering temperature of the comparative examples was measured to be about 950° C. or less. However, in these comparative examples, the dielectric constant was measured to be about 500 or less, or the dielectric loss was measured to be about 10% or more. Accordingly, the dielectric constant was shown not to be good when only one additive was used.

On the other hand, both CuBi₂O₄ and ZnO—B₂O₃—SiO₂ were used in the examples 1 to 32. As described in table 2, the sintering temperature was measured to be a relatively low temperature of about 950° C. or less. Also, the dielectric constant was about 500 or more. The dielectric loss was about 10 % on average. A dielectric composition having an excellent property capable of increasing the dielectric constant and reducing the dielectric loss while lowering the sintering temperature of the dielectric composition was found to be manufactured when both additives were used.

FIG. 2 is a scanning electron micrograph illustrating a sintered dielectric composition according to an embodiment of the present invention. In order to manufacture the dielectric composition, CuBi₂O₄ and ZnO—B₂O₃—SiO₃ are added to BaTiO₃ powder so as to be about 6 wt % and about 4 wt %, respectively. There is a micro structure generated by a sintering at a temperature of about 925° C. It was verified that a densification occurred together with a change of a particle shape. Accordingly, the dielectric composition according to the present invention was found to be sinterable at a low temperature of about 950° C. or less.

The dielectric composition according to the embodiments of the present invention can be sintered at a temperature of about 1,100° C. or less. Moreover, the dielectric having an excellent high temperature insulation resistance as well as satisfying X5R characteristics can be obtained.

If the multi-layer ceramic capacitor is manufactured using the dielectric composition, the BaTiO₃ dielectric layer can be uniformly sintered. As a result, a conglomeration of the internal electrodes can be suppressed by reducing a sintering shrinkage difference between the internal electrode and the dielectric layer. Accordingly, the short circuit rate can be minimized. At the same time, the electrostatic capacity can be maximized.

In addition, due to the improvement of the electrical properties and high-temperature insulation resistance, it is possible to manufacture a multi-layer ceramic capacitor having high reliability capable of satisfying X5R characteristics.

While the present invention has been shown and described in connection with the exemplary embodiments, it will be apparent to those skilled in the art that modifications and variations can be made without departing from the spirit and scope of the invention as defined by the appended claims. 

1. A dielectric composition comprising: a main component, BaTiO₃ of about 80 wt % or more; and an accessory component, CuBi₂O₄ and ZnO—B₂O₃—SiO₂-based glass of about 20 wt % or less.
 2. The dielectric composition of claim 1, wherein the content of CuBi₂O₄ is about 4 wt % to about 10 wt % relative to the total weight of BaTiO₃.
 3. The dielectric composition of claim 1, wherein the content of ZnO—B₂O₃—SiO₂-based glass is about 1 wt % to about 5 wt % relative to the total weight of BaTiO₃.
 4. The dielectric composition of claim 1, wherein the content of CuBi₂O₄ is about 6 wt % relative to a total weight of BaTiO₃, and the content of ZnO—B₂O₃—SiO₂-based glass is about 4 wt % relative to the total weight of BaTiO₃.
 5. The dielectric composition of claim 1, wherein the content of ZnO is about 50 wt % to about 90 wt % relative to the total weight of the glass.
 6. The dielectric composition of claim 1, wherein the mean particle diameter of BaTiO₃ is about 500 nm or less.
 7. The dielectric composition of claim 1, wherein a sintering temperature is about 600° C. to about 950° C.
 8. A multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate comprising: a ceramic laminated body laminated with a plurality of ceramic green sheets printed with a ceramic sheet internal electrode; a plurality of dielectric layers formed in the ceramic laminated body, the dielectric layers embedded with a multi-layer ceramic capacitor comprising a dielectric composition comprising a main component, BaTiO₃ of about 80 wt % or more and an accessory component, CuBi₂O₄ and ZnO—B₂O₃—SiO₂-based glass of about 20 wt % or less; and a plurality of capacitor internal electrodes formed between the dielectric layers, and electrically connected to the ceramic sheet internal electrode.
 9. The multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate of claim 8, wherein the content of CuBi₂O₄ is about 4 wt % to about 10 wt % relative to the total weight of BaTiO₃.
 10. The multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate of claim 8, wherein the content of ZnO—B₂O₃—SiO₂-based glass is about 1 wt % to about 5 wt % relative to the total weight of BaTiO₃.
 11. The multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate of claim 8, wherein the ceramic sheet internal electrode comprises one of Ag and Cu.
 12. The multi-layer ceramic capacitor embedded low temperature co-fired ceramic substrate of claim 8, wherein a firing temperature is about 600° C. to about 950° C. 